Product Features
· Good fluidity, easy to release bubbles, easy to pour. Simple operation and easy to demold.
· Rapid curing at room temperature.
· High tensile and tear strength, low shrinkage rate (≤0.3%).
· High number of mold releases (for example: gypsum products can be restored over 800 times).
· Good weather resistance, high temperature resistance, acid and alkali resistance, aging resistance.
Product Applications
· Mold making for products such as gypsum, GRC, cement, resin, etc.
· Molding of artificial stone, wax casting process.
· Mold making for architectural decoration products (such as eaves, fireplaces, wall decorations, planting containers, European-style furniture, furniture decorations, etc.).
· Mold making for unsaturated resin crafts, epoxy resin crafts, polyester resin crafts.
· Handcrafted soap and candle crafts, stationery gifts, and other craft industries.
· Mold making for casting statues, Buddha statues, Christmas ornaments, figures, etc.
· Can also be specially formulated according to customer product requirements.
Mold Silicone Operation
There are three mold opening methods for silicone molds: wrapping mold, brushing mold, and pouring mold. The wrapping mold operation method: the craft replica silicone is a flowing white liquid, divided into two groups: Group A is silicone, Group B is curing agent, for example: 100 grams of silicone plus 2% curing agent, stir evenly, pour into the prepared mold, and place it in a vacuum machine for vacuuming. After vacuuming, let the mold silicone cure naturally.
Reaction of silicone and curing agent ratio
· When the curing agent is added at 1%, the gel will still flow for 2.5 hours, and can be demolded in 6-8 hours.
· When the curing agent is added at 2%, the gel will still flow for 50 minutes to 1 hour, and can be demolded in 2-3 hours.
· When the curing agent is added at 3%, the gel will still flow for 28-30 minutes, and can be demolded in 1.5-2 hours.
· When the curing agent is added at 4%, the gel will still flow for 10-15 minutes, and can be demolded in 1-1.5 hours.
Mold Silicone Storage Instructions
· Shelf life: Below room temperature of 25°C, unopened packaging, 12 months.
· Packaging specifications: This product is packaged in iron barrels, with specifications of 25kg and 200kg.
· This product should be stored in a dry and sealed container at room temperature, and must not come into contact with water to prevent deterioration.
Product Parameter Table
Parameters of Series 6 Condensed Forming Translucent Mold Silicone (25°C)
Model |
610 |
615 |
620 |
625 |
630 |
640 |
650 |
660 |
Appearance |
White |
White |
White |
White |
White |
White |
White |
White |
Hardness (Shore Aº) |
10±2 |
15±2 |
20±2 |
25±2 |
30±2 |
40±2 |
50±2 |
60±2 |
Two-component mixing weight ratio (A:B) |
100:2/3 |
100:2/3 |
|
|
|
|
|
100:2/3 |
Dynamic viscosity (mPa.s) |
9600±2000 |
12000±2000 |
18000±2000 |
23000±2000 |
25000±2000 |
12000±2000 |
30000±2000 |
32000±2000 |
Tensile strength (MPa) |
2.4 |
2.8 |
3.7 |
4.5 |
4.3 |
4.2 |
2.1 |
1.8 |
Tear strength (kN/m) |
12±2 |
16±2 |
20±2 |
27±2 |
25±2 |
23±2 |
12±2 |
10±2 |
Elongation (%) |
320 |
389 |
440 |
550 |
560 |
580 |
180 |
160 |
Density (g/cm) |
1 |
1.05 |
1.05 |
1.12 |
1.13 |
1.14 |
1.16 |
1.18 |
Operation time (min) |
30-60 |
30-60 |
30-60 |
30-60 |
30-60 |
30-60 |
30-60 |
30-60 |
Curing time (h) |
4-6 |
4-6 |
4-6 |
|
4-6 |
|
|
|
Shrinkage rate (%) |
≤0.1 |
≤0.1 |
≤0.1 |
≤0.1 |
≤0.1 |
≤0.1 |
≤0.1 |
≤0.1 |
Parameters of Series 5 Condensed Forming Translucent Mold Silicone
Model |
510 |
515 |
520 |
525 |
530 |
540 |
550 |
560 |
Appearance |
White |
White |
White |
White |
White |
Product Images
Packaging Specifications:
Component A: 25KG/barrel 200KG/barrel
Component B: 1KG/bottle